Notes: the data is for reference only. Please consult our material engineers about specific use.
|
Item performance
|
Test condition
|
Test method
|
Data unit
|
Product designation
|
|
B2710G
|
B2718G
|
B2730G
|
|
Mechanical property
|
Tensile strength
|
23℃ (dry state)
|
ISO527
|
MPa
|
90
|
140
|
175
|
|
Elongation at break
|
23℃ (dry state)
|
ISO527
|
%
|
7.5
|
8
|
8
|
|
Bending strength
|
23℃ (dry state)
|
ISO178
|
MPa
|
120
|
160
|
220
|
|
Flexural modulus
|
23℃ (dry state)
|
ISO178
|
GPa
|
3.5
|
4.5
|
5
|
|
Non-notched impact strength
|
23℃ (dry state)
|
ISO179
|
KJ/m2
|
50
|
85
|
105
|
|
Notch impact strength
|
23℃ (dry state)
|
ISO179
|
KJ/m2
|
8
|
15
|
22
|
|
Glass fiber content
|
Dry state
|
ISO3451
|
%
|
10
|
18
|
30
|
|
Physical performance
|
Specific gravity
|
Dry state
|
ISO1183
|
g/cm3
|
1.20
|
1.25
|
1.36
|
|
Molding shrinkage
|
Dry state
|
|
%
|
---
|
---
|
---
|
|
Thermal performance
|
Melting range
|
Dry state
|
ISO3146
|
℃
|
225-255
|
225-255
|
225-255
|
|
Thermal deformation temperature
|
1.8Mpa
|
ISO75
|
℃
|
210
|
210
|
215
|
|
Electrical performance
|
Dielectric strength
|
Dry state
|
GB/T1408
|
MV/m
|
20
|
20
|
20
|
|
Volume resistivity
|
Dry state
|
GB/T1410
|
Ω.cm
|
1013
|
1013
|
1013
|
|
Other
|
Water absorption
|
|
|
%
|
1.25
|
1.25
|
1.25
|
|
Flame retardant property
|
Dry state
|
UL94
|
|
HB
|
HB
|
HB
|
|
| |
Notes: the data is for reference only. Please consult our material engineers about specific use.
|
Item performance
|
Test condition
|
Test method
|
Data unit
|
Product designation
|
|
B2710G
|
B2718G
|
B2730G
|
|
Mechanical property
|
Tensile strength
|
23℃ (dry state)
|
ISO527
|
MPa
|
90
|
140
|
175
|
|
Elongation at break
|
23℃ (dry state)
|
ISO527
|
%
|
7.5
|
8
|
8
|
|
Bending strength
|
23℃ (dry state)
|
ISO178
|
MPa
|
120
|
160
|
220
|
|
Flexural modulus
|
23℃ (dry state)
|
ISO178
|
GPa
|
3.5
|
4.5
|
5
|
|
Non-notched impact strength
|
23℃ (dry state)
|
ISO179
|
KJ/m2
|
50
|
85
|
105
|
|
Notch impact strength
|
23℃ (dry state)
|
ISO179
|
KJ/m2
|
8
|
15
|
22
|
|
Glass fiber content
|
Dry state
|
ISO3451
|
%
|
10
|
18
|
30
|
|
Physical performance
|
Specific gravity
|
Dry state
|
ISO1183
|
g/cm3
|
1.20
|
1.25
|
1.36
|
|
Molding shrinkage
|
Dry state
|
|
%
|
---
|
---
|
---
|
|
Thermal performance
|
Melting range
|
Dry state
|
ISO3146
|
℃
|
225-255
|
225-255
|
225-255
|
|
Thermal deformation temperature
|
1.8Mpa
|
ISO75
|
℃
|
210
|
210
|
215
|
|
Electrical performance
|
Dielectric strength
|
Dry state
|
GB/T1408
|
MV/m
|
20
|
20
|
20
|
|
Volume resistivity
|
Dry state
|
GB/T1410
|
Ω.cm
|
1013
|
1013
|
1013
|
|
Other
|
Water absorption
|
|
|
%
|
1.25
|
1.25
|
1.25
|
|
Flame retardant property
|
Dry state
|
UL94
|
|
HB
|
HB
|
HB
|
|
| |